Description
ERNiCrMo-13 is nickel-chromium-molybdenum alloy with an extra low carbon and silicon content.
Excellent corrosion resistance and high mechanical strength. Some typical base metals that this alloy is used on are ASTM and ASME B and SB 574, 575, 619, 622 and 626. It can equivalent to: Oxford Alloy 59.
Applications
ERNiCrMo-13 is used to weld low-carbon-nickel-chromium-molybdenum alloys, for welding the clad side of joints in steel clad with low-carbon-nickel-chromium-molybdenum alloys, and for welding low-carbon-
nickel-chromium-molybdenum alloys to steel and to other nickel-base alloys
Product Details
Chemical composition
| Grade |
Chemical composition(%) |
| ERNiCrMo-13 |
Mn |
S |
C |
Si |
P |
Ni |
Cr |
| ¡Ü0.5 |
¡Ü0.01 |
¡Ü0.01 |
¡Ü0.1 |
¡Ü0.015 |
Bal |
22~24 |
| Fe |
Cu |
Co |
Al |
Others |
Nb+Ta |
Mo |
| ¡Ü1.5 |
¡Ü0.5 |
¡Ü0.3 |
0.1~0.4 |
£¼0.5 |
1.8-2.5 |
15~16.5 |
Mechanical properties
| Tensile Strength |
Yield Strength |
Elongation |
| 700Mpa |
400Mpa |
30% |
Welding paramaters
| Process |
Diameter |
Voltage |
Amperage |
Gas |
| TIG |
.045¡± (1.2mm) |
13-16 |
80-110 |
100% Argon |
| 1/16¡± (1.6mm) |
14-18 |
90-130 |
100% Argon |
| 3/32¡± (2.4mm) |
15-20 |
120-175 |
100% Argon |
| 1/8¡± (3.2mm) |
15-20 |
150-220 |
100% Argon |
| MIG |
.045¡± (1.2mm) |
28-32 |
180-220 |
75% Argon + 25% Helium |
| 1/16¡± (1.6mm) |
29-33 |
200-250 |
75% Argon + 25% Helium |
| SAW |
3/32¡± (2.4mm) |
28-30 |
275-350 |
Suitable Flux may be used |
| 1/8¡± (3.2mm) |
29-32 |
350-450 |
Suitable Flux may be used |
| 5/32¡± (4.0mm) |
30-33 |
400-550 |
Suitable Flux may be used |
Specifications
AWS A5.14, SFA 5.14, F-No. 43 UNS N06059
|